Experiments show lead-free pastes will give great results with 0201s
4 October 2006Manufacturing / Production Technology, Hardware & Services
DEK has concluded research into screen printing for 0201 SMT components using SnPb and SAC solder pastes, highlighting new assembly and board design parameters for robust, high-volume assembly with minimal application-specific modifications. Among the observations from analysing a large number of test assemblies post reflow, DEK found that SAC pastes have an inherently wider process window.
Following the research, the optimum pad size for 0201 assembly is now known to be 300 x 380 x 230 µm, with pad-to-pad spacing of 200 µm. No-clean paste and air reflow atmosphere produce the least tombstone defects. Technologies that increase wetting forces, such as nitrogen reflow or water soluble pastes, induce more defects. Better yields were experienced with SAC-based pastes, because the wetting forces are lower with lead-free formulae. "Assembly conditions that promote slower wetting speeds create a larger process window and produce good yield, and this is largely independent of the component orientation," said Clive Ashmore, and one of the leaders of the research team.
After establishing design and process parameters that produced the minimum number of defects, the experiments then applied very challenging assembly scenarios to discover the limits at which defects begin to occur. Pad spacing was also reduced to 100 μm to encourage bridging. In addition, the overlap between the end terminations of the components and the solder paste, which is known as the 'grab', was tested at 150, 100 and 50 μm. To provoke tombstone defects, stencil registration was deliberately offset to create an imbalance in the grab between the two terminations of the same component. Registration errors of 0, 1,0 and 1,5 μm in both x- and y-axes were deliberately applied, to determine tolerances for printing accuracy for successful 0201 assembly.
The results showed that the tombstoning defects caused by increasing stencil offset can be reduced by increasing grab. On the other hand, a large grab increases bridging defects and solder balling. "High printing accuracy and low grab are required to minimise the cumulative defects arising from tombstoning, bridging and solder balling," explained Ashmore.
After printing SAC-based paste at the 4-mil print offset condition, post-reflow yield generally surpassed the performance of the tin-lead eutectic solder assemblies. Tombstoning and solder-balling levels were also significantly lower. "These results show great promise for assembling 0201s with SAC-based pastes," concluded Ashmore.
The impact of harsh environments and ionic contamination on post-reflow circuit assemblies MyKay Tronics
Manufacturing / Production Technology, Hardware & Services
There is well documented historical proof that post-reflow circuit assemblies, when subjected to harsh environments, are particularly vulnerable to failure mechanisms, but modern electronic assemblies are far more susceptible to this phenomenon.
Read more...Engineering copper grain structure for high-yield hybrid bonding in 3D packaging Testerion
Editor's Choice Manufacturing / Production Technology, Hardware & Services
The way copper grains are sized and distributed forms the metallurgical foundation of hybrid bonding, enabling lower bonding temperatures, greater reliability, and stable grain structures throughout integration.
Read more...Understanding solder dross: causes and control strategies Truth Electronic Manufacturing
Editor's Choice Manufacturing / Production Technology, Hardware & Services
Dross formation is an inevitable consequence of wave soldering. It occurs when molten solder comes into contact with oxygen, forming metal oxides that float on the surface of the solder bath. Over time, this oxidation byproduct accumulates and must be removed to maintain solder quality and process consistency.
Read more...Implications of using Pb-free solders on X-ray inspection of flip chips and BGAs MyKay Tronics
Manufacturing / Production Technology, Hardware & Services
With the move to Pb-free soldering, most of the attention has been paid to reflow temperatures, component compatibility, and reliability concerns, but the implications for inspection, particularly X-ray inspection, are equally important and often underestimated.
Read more...The causes of solder balls in robotic soldering
Manufacturing / Production Technology, Hardware & Services
Solder balls (also known as solder splatter) are a major concern in many production sites as they may potentially cause shorts, leading to long-term impacts on product reliability.
Read more...Material challenges for superconducting quantum chips
Manufacturing / Production Technology, Hardware & Services
To achieve the scalable and repeatable production of superconducting circuits for quantum technology products, players in the industry are leveraging semiconductor fabrication techniques.
Read more...UV curing oven for high-efficiency PCB production Techmet
Manufacturing / Production Technology, Hardware & Services
The jCURE-2UV+ from JTU is a cutting-edge ultraviolet curing oven engineered for fast, reliable curing of UV-sensitive coatings in SMT production environments.
Read more...Automatic stencil cleaning ZETECH ONE
Manufacturing / Production Technology, Hardware & Services
The MBtech N29 series delivers high-precision stencil cleaning with a focus on efficiency, economy and the environment, and is ideal for SMT adhesive and solder paste stencil maintenance.
Read more...Versatile wave soldering MyKay Tronics
Manufacturing / Production Technology, Hardware & Services
The EMST Stallion fc - PLC is a highly capable wave soldering machine engineered for precision and productivity in electronics manufacturing.
While every effort has been made to ensure the accuracy of the information contained herein, the publisher and its agents cannot be held responsible for any errors contained, or any loss incurred as a result. Articles published do not necessarily reflect the views of the publishers. The editor reserves the right to alter or cut copy. Articles submitted are deemed to have been cleared for publication. Advertisements and company contact details are published as provided by the advertiser. Technews Publishing (Pty) Ltd cannot be held responsible for the accuracy or veracity of supplied material.
printer friendly version